| Special Application Product |
 |
| DESCRIPTION AND APPLICATIONS |
| Powder Content |
Description |
Composition |
Purpose |
| Calcium Silicon |
CaSi Cored Wire |
30%Ca, 60%Si |
Melting flux for modification of inclusion for improvement of mechanical properties and avoiding nozal clogging in CC. |
| Calcium Iron |
CaFe Cored Wire |
30%Ca, 70% Fe |
For melts with low silicon content. e.g. steel tubes, free cutting steel, drop forging die steel, deep drawing steel, etc. |
| Calcium Aluminium Iron |
CaFeAl Cored Wire |
30%Ca, 25%A1, Bal.Fe |
Application is same as above and for deoxidation. |
| Calcium |
Ca Cored Wire |
Ca : ≥98% |
Application is same as above with low silicon content and for calcium treatment. |
Aluminium
(Solid Wire) |
Al Solid Wire |
Al 99% |
Application is for de-oxidation and alloying addition. |
Aluminium
(Cored Wire) |
Al Cored Wire |
Al 98% |
Application is for de-oxidation and alloying addition. |
|
|
Metallurgical Cored Wires are manufactured from high quality rolling steel strips to make tubes and filled tightly with compounded alloy material on highly precision machine.
Different grades of Metallurgical Cored Wires are available in Cored Coils form of following dimension 9.0MM, 13MM, 16MM Diameter as well as 5 mm for investment casting processes. |
|
| |
OUTSIDE DIAMETER (MM) |
INSIDE DIAMETER (MM) |
WIDTH (MM) |
| BIG COIL |
1200 |
600 |
1050 |
| SMALL COIL |
1200 |
600 |
700 |
|
1. Metallurgical Cored Wires are available with horizontal & vertical types of flipping
2. Metallurgical Cored Wires are generally manufactured in 9.00 mm 13.00 mm and 16.00 mm diameter. Cored Wires in other diameters and grades
can also be manufactured on special requirements by the user
3. The maximum weight of an individual Metallurgical Cored Wire Coil is 2.00 M.T |
|
PRECAUTIONS
Metallurgical Cored Wires are supplied with steel frame support / wooden pallet with moisture proof film wrapped around it to protect it from atmospheric attack. However, it is advised to store cored wire in dry area. |